Graft Co-Polymer Nano Particle as Carbon Steel Corrosion Inhibitor in 1M H2SO4 At 293K

Document Type : Original Article

Authors

1 Chemistry Department, College of Education for Pure Sciences, University of Kerbala, Kerbala/ Iraq

2 Department of Chemistry,College of Education for pure sciences,Kerbala of University, Karbala,Iraq

3 Hilla University college

Abstract

New graft co-polymer nano-particle (coating nano-polymer) was prepared as a corrosion inhibitor in 1M sulfuric acid. The synthesized coating nano-polymer was characterized by FT-IR, 1H NMR and atomic force microscope (AFM). Synthesized coating nano-polymer mixed with acrylic acid in different proportion (0.2-0.8 mole: 293K: 30 min). Potential-dynamic polarization technique is used to get current corrosion, inhibition efficiency, cathodic and anodic Tafel slopes with examination of concentration influence on inhibition efficiency, the results revealed that the inhibition efficiency increases as inhibitor concentration increases. The maximum inhibition recorded efficiency 93% at 0.8 mol.

Keywords

Main Subjects